Waveplate

Double Convex Lenses are used in image relay applications, or for imaging objects at close conjugates. Double Convex Lenses have positive focal lengths, along with two convex surfaces with equal radii. Aberrations will increase as the conjugate ratios increase.  Double-Convex Lenses are used in a range of industries or applications. HG OPTRONICS offers Double Convex lenses with a variety of coating options.

Er: YAG (Erbium-doped Yttrium Aluminum Garnet) is a solid-state crystal widely used as a laser medium in various medical and dental applications. It is made by doping erbium ions into yttrium aluminum garnet (YAG) crystals and can emit laser light with a wavelength of approximately 2.94 micrometers in the infrared spectrum.

HGO grows BBO Nonlinear crystals using flux technology. BBO crystal transparency ranges from 188 nm to 5,2 µm, which includes reasonable transparency from 3-5,2 µm for few tens µm thick crystals, while their phase-matchable range spans almost over the entire transparency range. Combined with other magnificent properties of BBO, it is favorable for numerous nonlinear parametric applications. It is worth to mention that BBO crystals have the highest nonlinearity in the UV range out of all common nonlinear crystals.

Calcium Fluoride windows and lenses for UV and IR spectrum. Custom made CaF2 windows, CaF2 lenses and wedges according to customer's specifications. CaF2 windows up to 220mm diameter; CaF2 wedges, prisms and CaF2 mirrors; Excimer CaF2 optics, Raman grade CaF2 optics and etc.

HGO grows LiF crystals in house using Czochralski technology. LiF crystal or lithium fluoride crystal is an optical material with outstanding transmittance in VUV region. It is also used for windows, prisms, and lenses in the visible and infrared in 0.104µm-7µm. LiF single crystal is sensitive to thermal shock and would be attacked by atmospheric moisture at 400°C. When working at a high temperature of 600°C, the LiF crystal softens and is slightly plastic, so it can be bent into radius plates. In addition irradiation produces color centers. Hence, users should take measures to protect LiF crystals from moisture and high energy radiation damages. What is more LiF can be cleaved along (100) plane and less commonly (110) plane. The optical characteristics are good and yet the structure is not perfect and cleavage is difficult.

Potassium Gadolinium Tungstate (KGd(WO₄)₂) crystal is an excellent stimulated Raman laser crystal with characteristics such as a wide light transmission range, good thermal conductivity, high damage threshold, large Raman shift coefficient, and high Raman gain. It can maintain high conversion efficiency and beam quality during the Raman frequency conversion process. The KGW crystal can withstand high pump power and is suitable for pump lights of various wavelengths, making it widely used in Raman lasers, laser frequency conversion, medical imaging, photodynamic therapy, environmental monitoring, spectroscopy research, material processing, and other fields.

Our beamsplitter plates can be used in high power laser system. When using beamsplitter plates, it is important to make it in mind that the two partial beams travel in different optical paths. The optical paths depend on the incident angle and the thickness of plates.

Germanium (Ge) is the preferred lens and window material for high performance infrared imaging systems in the 8–12 um wavelength band.