Crystals and optics processing services

HGO grows LiF crystals in house using Czochralski technology. LiF crystal or lithium fluoride crystal is an optical material with outstanding transmittance in VUV region. It is also used for windows, prisms, and lenses in the visible and infrared in 0.104µm-7µm. LiF single crystal is sensitive to thermal shock and would be attacked by atmospheric moisture at 400°C. When working at a high temperature of 600°C, the LiF crystal softens and is slightly plastic, so it can be bent into radius plates. In addition irradiation produces color centers. Hence, users should take measures to protect LiF crystals from moisture and high energy radiation damages. What is more LiF can be cleaved along (100) plane and less commonly (110) plane. The optical characteristics are good and yet the structure is not perfect and cleavage is difficult.

A Neutral Density filter allows a photographer to control the exposure in an image very easily. The filter stops light reaching the camera sensor, therefore allowing us to leave the camera with a higher aperture for a longer amount of time. HG OPTRONICS neutral-density filter is a filter that reduces or modifies the intensity of all wavelengths, or colors, of light equally, giving no changes in hue of color rendition.

HGO grows BBO Nonlinear crystals using flux technology. BBO crystal transparency ranges from 188 nm to 5,2 µm, which includes reasonable transparency from 3-5,2 µm for few tens µm thick crystals, while their phase-matchable range spans almost over the entire transparency range. Combined with other magnificent properties of BBO, it is favorable for numerous nonlinear parametric applications. It is worth to mention that BBO crystals have the highest nonlinearity in the UV range out of all common nonlinear crystals.

α-BBO (α-BaB2O4) is a negative uniaxial crystal which has large birefringence over a broad transparent range of 190nm to 3500nm. α-BBO is an excellent crystal especially in UV and high power applications. The physical, chemical, thermal, and optical properties of alpha-BBO crystal are similar to those of Beta-BBO. However, there is no second order nonlinear effect in alpha-BBO crystal due to the centrosymmetry in its crystal structure and thus it has no use for second order nonlinear optical processes. Instead, alpha-BBO is widely used for fabrication of polarizers, polarizing beam displacers, phase retarders, birefringent plates, and time delay compensators especially those for UV and high power lasers.

BK7 window is the most common type of window. It has good performance over visible and near infrared wavelength regions. At the same time, BK7 window is ideal for applications require minimal transmitted beam deviation. It is suitable for AR coating.

HGO grows Nd:YLF laser crystals using Czochralski technology. Nd3+:YLF crystal is characterized by its long lifetime of 4F3/2 neodymium energy level. Compared to Nd:YAG, the lower thermal conductivity and a weak negative dn/dT lead to lower thermal distortions and allow to achieve a better output beam quality. Another distinctive feature is the high UV transparency, which is favorable for pumping with xenon flash lamps.

Laser mirrors are fabricated with specialized coatings, which will offer high damage thresholds.

LiNbO3 is widely used as electro-optic modulators and Q-switches for Nd:YAG, Nd:YLF and Ti:Sapphire lasers as well as modulators for fiber optics.