Cr4+:YAG crystals Chromium Doped Yttrium AIuminum Garnet

Co2+:MgAl2O4 Cospinel is a relatively new material for passive Q-switching in lasers emitting from 1.2 to 1.6 μm, in particular, for eye-safe 1.54 μm Er:glass laser, but also works at 1.44 μm and 1.34 μm wavelengths. Spinel is a hard, stable crystal that polishes well. Cobalt substitutes readily for magnesium in the Spinel host without the need for additional charge compensation ions. High absorption cross section (3.5×10-19 cm2) permits Q-switching of Er:glass laser without intracavity focusing both with flash-lamp and diode-laser pumping. Negligible excited-state absorption results in high contrast of Q-switch, i.e. the ratio of initial (small signal) to saturated absorption is higher than 10.

The Positive Meniscus Lenses are a convex-concave lens, but it is thicker at the center than at the edges. They are felt polished and are used universally in the ophthalmic industry where convention dictates that lens power be specified in Diopters. The Negative Meniscus Lenses are a convex-concave lens, but it is thinner at the center than at the edges. Otherwise description is similar to Plano Concave lenses.  

A cylindrical lens is a lens that focuses light on a line instead of a point, like a spherical lens. The curved face or faces of a cylindrical lens are sections of a cylinder, and focus the image passing through it into a line parallel to the intersection of the surface of the lens and a plane tangent to it. The lens compresses the image in the direction perpendicular to this line and leaves it unaltered in the direction parallel to it (in the tangent plane). In a light sheet microscope, a cylindrical lens is placed in front of the illumination objective to create the light sheet used for imaging. Cylindrical lenses focus or expand light in one axis only. They can be used to focus light into a thin line in optical metrology, laser scanning, spectroscopic, laser diode, acousto-optic, and optical processor applications. They can also be used to expand the output of a laser diode into a symmetrical beam. Cylindrical lenses are widely used in telecom applications like WSS, 40G/100G modules and laser applications like pump laser modules

Ytterbium-doped Potassium Gadolinium Tungstate (Yb:KGd(WO₄)₂, Yb:KGW) crystal is an excellent laser gain material, boasting numerous advantages over the widely used Nd³⁺-doped materials. Its wide spectral emission band of 1023-1060 nm enables the generation of short laser pulses (picosecond or femtosecond level). The broad absorption band at 980 nm and highly absorbent pump radiation allow it to efficiently utilize diode laser pumping. Compared with YAG doped with Yb³⁺ ions, KGW crystal has a larger absorption cross-section, which reduces the minimum pump intensity required to achieve transparency in the quasi-two-level system of Yb.

The Yttrium Orthovanadate (YVO4) is a positive uniaxial crystal grown with Czochralski method. It has good temperature stability and physical and mechanical properties. It is ideal for optical polarizing components because of its wide transparency range and large birefringence. It is an excellent synthetic substitute for Calcite (CaCO3) and Rutile (TiO2) crystals in many applications including fiber optic isolators and circulators, interleavers, beam displacers and other polarizing optics.

HGO have advanced coating machines which can meet endusers’different application requirement. We can very high laser induced damaged threshold coating with IAD, EB and IBS coating techniques , also Cr-Au, Aluminum and silver mental coating can also be available in HGO. Customers are very welcome to contact with us for further information.

HGO grows Pr:YLF laser crystals using Czochralski technology. Pr3+:YLF has been found as promising laser material for producing visible lasers directly and UV lasers through intracavity second-harmonic generation. Very few laser materials have the necessary properties for the realization of lasing in the visible spectral range. Trivalent praseodymium (Pr3+) is known to be an interesting laser ion for use with solid-state lasers in the visible spectral range because of its energy levels scheme, providing several transitions in the red (640 nm, 3P0 to 3F2), orange (607 nm, 3P0 to 3H6), green (523 nm, 3P0 to 3H5), and dark red (720 nm, 3P0 3F3+3F4) spectral regions.

Er: YAG (Erbium-doped Yttrium Aluminum Garnet) is a solid-state crystal widely used as a laser medium in various medical and dental applications. It is made by doping erbium ions into yttrium aluminum garnet (YAG) crystals and can emit laser light with a wavelength of approximately 2.94 micrometers in the infrared spectrum.